High Hardness: Surface hardness of casting iron balls is more than HRC 56.
Low Broken Rate: The actual broken rate is not higher than 1%;
Good Wear-resistant: 30-50g/ton in cement industry, 350-430g in gold mines
High Hardness: Surface hardness of casting iron balls is more than HRC 56.
Low Broken Rate: The actual broken rate is not higher than 1%;
Good Wear-resistant: 30-50g/ton in cement industry, 350-430g in gold mines
EO CASTINGS grinding balls are widely used in mining, power plant, cement and magnetic materials industries.
In the using process, the surface hardness getting higher and the wear resistant getting strengthen, at the same time, the production capacity of ball mill getting improved.
Products Specifications
Common Names | High Chrome Grinding Cylpeb | ||||||||||||
Main Materials | High Chromium Castings | ||||||||||||
Chemical Composition(%) | C | Si | Mn | Cr | Mo | Cu | P | S | |||||
2.0-3.2 | 0.3-1.2 | 1.3-2.6 | 10-15 | ≤2.0 | ≤1.0 | ≤0.10 | ≤0.08 | ||||||
Mechanical Properties | Microstructure | Hardness(HRC) | |||||||||||
M+C | ≥56 | ||||||||||||
Diameter Tolerance(mm) | Φ8*10 | Φ10*12 | Φ12*14 | Φ14*16 | Φ16*18 | Φ18*20 | |||||||
Φ20*25 | Φ25*30 | Φ30*35 | Φ35*40 | Φ35*45 | |||||||||
NOTE: If modulating needed, metamorphic chemical ingredients&other alloying elements vary from products above, price would be as contract signed.